The impact of carbon coating on the synthesis and properties of α’’-Fe16N2 powders

C.A. Bridges, O. Rios, L.F. Allard, H.M. Meyer, III, A. Huq, Y. Jiang, J.-P. Wangd, M.P. Brady, 2016
Fusion TEM holder tip
Image courtesy of Phys. Chem. Chem. Phys.

Abstract

This paper presents the preparation of carbon composite Fe16N2 powders, and the influence of a protective carbon coating on the yield and magnetic properties of Fe16N2. Nanoparticle precursors with and without carbon were reacted under ammonia gas flow to produce Fe16N2. Neutron and X-ray powder diffraction indicate that the powders contain typically 40-60% Fe16N2, with the remaining phases being unreacted iron, Fe4N or Fe3N. Transmission electron microscopy demonstrates that the carbon coating is effective at reducing the level of sintering of Fe nanoparticles during the reduction stage prior to ammonolysis. XPS results support the retention of a carbon coating on the surface after ammonolysis, and that there is Fe-C bonding present at the particle surface. In situ TEM was used to observe loss of ordering in the nitrogen sublattice of carbon composite Fe16N2 powders in the range of 168 °C to 200 °C. Magnetic susceptibility measurements show maximum values for saturation magnetization in the range of 232 emu g(-1), and for coercivity near 930 Oe, for different samples measured up to 2 T applied field at 300 K.

Impact Statement

High temperature in situ TEM was used to study thermal stability of α’’-Fe16N2 . It was shown that that the carbon coating is effective at reducing the level of sintering of Fe nanoparticles during the reduction stage prior to ammonolysis. Loss of ordering in the nitrogen sublattice of carbon composite Fe16N2 powders in the range of 168 °C to 200 °C was observed.